Small ceramic rod stick 0.5mm 3mm 5mm zirconia alumina precision rods
Materials：Alumina (Al2O3)/ Zirconia(ZrO2) /Si3N4 /SiC ...etc
Sizes：Mini-OD: 0.02mm;Max-length: 500mm
Delivery times：2 -25 days(depends on the quantity)
Precision：Ra 0.1um tolerance: 0.001mm... etc
Features：Heat resistance / Wear resistance / High purity / Refractory / High Corrosion / Good Insulation
Customized：Can be custom for special sizes and shapes
1. Factory price and shipment within 24 hours In stocks
2. MOQ:1qty
3. Payment Term: PayPal; T/T; L/C etc.
4. Shipment: by sea by air by courier by post etc.
Ceramic plates sheet substrate disc series
Small ceramic rod stick 0.5mm 3mm 5mm zirconia alumina precision rods
As a Professional Advanced Technology Ceramic Manufacturers,
Us Support To Customize Different Specifications Of Ceramic Components
Feature:
1.Refractory, High Temperature Resistance, Maximum Used Temperature: 1800 ºC (3272ºF)...
2. Hardness Strength, Wear Resistance Up To Mohz 9.0; HRA 80-90...
3. High Voltage, Good Insulation Performance ,Electrical Resistivity Up To 10∧14 Ohm.Cm...
4. High Polished Surface Up To Rz0.8(Ra0.1) ...
5. Superior Mechanical Strength, Max 10 MPa.m1/2 Fracture toughness,
6. Pressure Resistance, Max 2300MPa compressive strength...
7. Anti-High Corrosion Resistance, Such As Acid Alkali Resistance...
8. Long Service Life...
9. Other excellent property
Dimension and tolerance:
·Diameter as small as 0.2mm， depends on length
·Length as long as 400mm, as short as 0.5mm
·Diameter tolerance we could make as fine as 0.001mm
Additional Information:
·Discounts on large quantities of Ceramic Rod
·In stock items will typically ship in a few working days.
·Unit price and estimated ship dates will be calculated when the length and quantity are specified.
·The length and special sizes can be customized
High heat and temperature:
The ceramic have a excellent high heat temperature resistant ability. Small ceramic rod can be used under 1800 ℃ high temperature environment.up to 10∧13 Coefficient of thermal expansion ( 10∧6) from 20 - 1000°C. up to 2800°C Melting point.
Wear Hardness abrasion:
The ceramic is better wear and abrasion resistant property than metal. The ceramic hardness (mohs)up to 9, HRA 80-90.
Ceramic hardness is not second only to diamond, but far beyond the wear resistance of steel and stainless steel
Application Of; Small Ceramic Rod Stick:
1. mining industry
2. Cement industry
3. Coal handling industry
4. Steel industry
5. Port industry
6. Power plant
7. Others
The properties of ceramics
· Flexural strength· Chemical resistance· Electrical insulation;· Corrosion resistance
· Wear resistance· Temperature resistance· Thermal conductivity· High voltage· Hardness...
Ceramic materials
· 95%--99.99% Alumina (Al2O3)
· Silicon Carbide
· Silicon Nitride
· TTZ: Magnesia partially stabilized Zirconia (ZrO2)
· YTZP: Yttria partially stabilized Zirconia (ZrO2)
· ZDY: Yttria fully stabilized Zirconia (ZrO2)
| Properties | Units | AL2O3 | ZrO2 | SiC | Si3N4 |
| Density | g/cm³ | 3.65-3.93 | 5.95-6.0 | 3.12 | 3.23 |
| Water absorption | 0 | 0 | 0 | 0 | 0 |
| Coefficientof thermal expansion | 10-16/k | 7.9-8.5 | 10.5 | 3 | 3.2 |
| Modulus of elasticity young`s mod | GPa | 280-340 | 210 | 440 | 300 |
| Poission`s ratio | / | 0.21-0.22 | 0.3 | 0.17 | 0.26 |
| HV hardness hv | MPa | 1650 | 1300-1365 | 2800 | 1500 |
| Flexural strength | MPa | 310 | 950 | 390 | 720 |
| Flexural strength(700℃) | MPa | 230 | 210 | 380 | 450 |
| Compressive strength | MPa | 2200 | 2000 | 1800 | 2300 |
| Fracture toughness | MPa*m1/2 | 4.2 | 10 | 3.9 | 6.2 |
| Heat conductivity | W/m*k | 26-30 | 2-2.2 | 120 | 25 |
| Electrical resistivity | Ω*mm2/m | >1016 | >1015 | >103 | >1013 |
| Max use temperature | ℃ | 1750 | 1050 | 1550 | 1050 |
| Resistance to acid alkaline | / | high | high | igh | high |
| Dielectric constant | / | 9.6 | 9 | 9.66-10.03 | |
| Dielectric strength | KV/mm | 8.7 | 9 | / | |
| Thermal shock resistance | △T（℃） | 180-220 | 280-350 | 230-260 | / |
| Tensile strength | MPa | 248 | 250 | / | / |
| Precision of manufacture | |
| Dimensional accuracy | Up to 0.001mm |
| moothness | Highest possible mirror |
| Concentricity | Up to 0.003mm |
| Parallelism | Up to 0.002mm |
| The inner hole tolerance | The minimum 0.005mm |
| Straight flute | e narrowest 0.1x100mm |
| The thickness of the size | Minimum to 0.02mm |
| The screw thread | Minimum internal thread M2 |
| Cylindricity | Up to 0.004mm |
| The linear tolerance | Up to 0.001mm |
| The smallest aperture | The minimum 0.07mm |
| ecision process | CNC maching,grinding,lapping |
| Surface finish | Glazed,polishing or metallized |
Visual quality: 1. No cracks, no dark dots, no contamination and sharp edges; 2. Evenly distributed glaze with very smooth surface | |
Customization & Machining Service
As a professional manufacturer of industrial ceramic components.We can custom the sepcial specifications of ceramic plates,blocks or other ceramic parts.High quality,Factory price, on-time delivery, High composition of ceramics
FAQ
1. Monthly Capacity: 50,000-60,000 pcs;
2. Material: OEM or as per your suggestion;
3. Lead time: about 7-10 days, pls confirm the quantities required;
4. Incoterm: FOB, CFR, CIF;
5. Delivery Cost: It is determinated by the destination port;
6. Payment Term: PayPal; T/T; L/C.
7. Shipment: by sea, by air, by courier, by post, etc.
Feedback
1. For any query or doubt, please contact us firstly, we will update with you soon;
2. For any other satisfaction, please also feedback to us, which could improve our service better and better.
For more information about ceramics parts,please contact our engineers in time >>>